mill sintron®

CoCr dry mill - easy as wax

Ceramill Sintron revolutionises CNC-based dry processing of non-precious metal restorations using desktop milling machines in-house in the laboratory. The wax-like texture of Ceramill Sintron allows the material to be dry milled effortlessly. During the subsequent sintering process under shielding gas atmosphere the frameworks achieve their final material properties – a CoCr unit with very homogeneous material structure. Any conventional CoCr framework porcelain can then be used for veneering. Ceramill Sintron was developed in collaboration with the Fraunhofer IFAM Dresden, Germany.

  • Crowns & Bridges, anatomically reduced & fully anatomical
  • Telescope
  • Multi-unit, screw-retained restorations on titanium
  • Custom abutments on titanium bases
  • Anatomically reduced and fully anatomical crown and bridge frameworks in the anterior and posterior region
  • Effortless dry milling and minimum cutter wear thanks to wax-like texture
  • Comfortable handling due to easy reworking and finishing of the milled framework in the green state
  • Maximum process reliability thanks to homogeneous, distortion-free frameworks
  • Excellent strength values, bonding strength and biocompatibility
  • Tensile Strength: 900 MPa
  • Modulus of Elasticity: 200 GPa
  • Density: 7.9 g/cm3
  • Vickers Hardness: 270 HV 10
  • CTE 25 - 500 °C: 14,5 *10-6/K
  • Elongation at rupture: 30 %
  • Open porosity: 0 %
  • Color: silver
  • Oxide color: grey-green
  • Proof stress (Rp 0,2%): 450 MPa
  • Co: 66
  • Cr: 28
  • Mo: 5
  • Si: < 1
  • Fe: < 1
  • Mn: <1
  • In accordance with DIN EN ISO 22674:2007 the alloy is free of nickel, beryllium, gallium and cadmium